Fluorosilicone rubber
Fluosilicone rubber combines the advantages of silicone rubber and fluorine rubber, with excellent resistance to fuel oil, machine oil, solvents, and chemical media.
Applications
- Aviation
- Automotive
- Health care
Technical Indexes
General purpose Fluorosilicone rubber
Type Grade Name Hardness (Shore A) Tensile strength (Mpa) Elongation at break % Tear strength (KN/m) Compression set% 175℃，22h General purpose (translucent) XTF1030-40 40±5 ≥9.0 ≥350 ≥20 ≤20 XTF1030-50 50±5 ≥9.0 ≥300 ≥20 ≤20 XTF1030-60 60±5 ≥9.0 ≥250 ≥20 ≤20 XTF1030-70 70±5 ≥8.0 ≥200 ≥15 ≤20 XTF1030-80 80±5 ≥7.0 ≥150 ≥15 ≤20
*DBPH 0.5%, press cure: 10min/175℃, post
cure: 4h/200℃ (DCBP or platinum catalyst for extrusion)
High-rebound Fluorosilicone rubber
Type | Grade Name | Hardness (Shore A) | Tensile strength (Mpa) | Elongation at break % | Tear strength (KN/m) | Compression set% 175℃，22h | |
High rebound and low compression set (translucent) | XTF1040-30 | 30±5 | ≥9.0 | ≥400 | ≥15 | ≤10 | |
XTF1040-40 | 40±5 | ≥10.0 | ≥400 | ≥20 | ≤10 | ||
XTF1040-50 | 50±5 | ≥10.0 | ≥350 | ≥20 | ≤10 | ||
XTF1040-60 | 60±5 | ≥10.0 | ≥330 | ≥20 | ≤10 | ||
XTF1040-70 | 70±5 | ≥10.0 | ≥250 | ≥15 | ≤10 | ||
XTF1040-80 | 80±5 | ≥8.0 | ≥150 | ≥15 | ≤10 | ||
*DBPH 0.5%, press cure: 10min/175℃, post cure: 4h/200℃
Bonding purpose Fluorosilicone rubber
Type Grade Name Hardness (Shore A) Tensile strength (Mpa) Elongation at break % Tear strength (KN/m) Compression set% 175℃，22h Bonding purpose (translucent) XTF1050-60 60±5 ≥8.0 ≥300 ≥20 ≤12 XTF1050-70 70±5 ≥8.0 ≥300 ≥20 ≤12
*DBPH 0.5%, press cure: 10min/175℃,
post cure: 4h/200℃
High tear strength Fluorosilicone rubber
Type Grade Name Hardness (Shore A) Tensile strength (Mpa) Elongation at break % Tear strength (KN/m) Compression set% 175℃，22h High tear strength (translucent) XTF1060-40 40±5 ≥10.0 ≥400 ≥40 ≤25 XTF1060-50 50±5 ≥10.0 ≥350 ≥40 ≤25 XTF1060-60 60±5 ≥10.0 ≥330 ≥40 ≤25 XTF1060-70 70±5 ≥9.0 ≥250 ≥35 ≤25 XTF1060-80 80±5 ≥8.0 ≥150 ≥30 ≤25
*DBPH 0.5%, press cure: 10min/175℃,
post cure: 4h/200℃